Long Carbon Fiber Reinforced Composite
Long Carbon Fiber Reinforced Composite
Long carbon fiber reinforced thermoplastics are fiber-reinforced composite materials known for high mechanical strength, excellent stiffness, lightweight performance, and good dimensional stability. They are widely used in demanding industrial, automotive, and mechanical applications where enhanced structural performance is required.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 200 - 300 MPa |
| Tensile Modulus | 15,000–35,000 MPa |
| Elongation at Break | 1-3% |
| Flexural Modulus | 15,000–30,000 MPa |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point (PA66) | 255 - 265 °C |
| Melting Point (PA6) | 220 - 225 °C |
| Heat Deflection Temperature, 0.45 MPa | 200–250°C |
| Heat Deflection Temperature, 1.82 MPa | 180–230°C |
| Continuous Service Temperature | 100–150°C |
| Flammability (UL94) | HB (V-0 grades available) |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 - 100°C |
| Drying Time | 4 - 8hrs |
| Melt Temperature (PA66) | 280 - 310 °C |
| Mold Temperature | 80 - 100 °C |
| Injection Pressure | 80–140 MPa |
PDF Download
Long Carbon Fiber Reinforced Composite Technical Datasheet
Download the complete technical datasheet including mechanical, thermal, and processing properties.