Antistatic PA6
Polyamide PA6 - Antistatic Modified Nylon
Antistatic PA6 is a modified nylon material developed to reduce static electricity accumulation and provide reliable electrostatic protection. It maintains the excellent mechanical strength, wear resistance, chemical resistance, and dimensional stability of standard PA6 while offering controlled electrical resistance performance.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 80 MPa |
| Tensile Modulus | 2,900 MPa |
| Elongation at Break | 50% |
| Hardness (Rockwell) | R110 / R120 |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point (PA66) | 255 - 265 °C |
| Melting Point (PA6) | 215 - 225 °C |
| HDT (1.82 MPa, PA66) | 70 - 90 °C |
| HDT (1.82 MPa, PA6) | 65 - 80 °C |
| Continuous Use Temp (PA66) | 80 - 120 °C |
| Flammability (UL94) | HB (V-0 grades available) |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 °C |
| Drying Time | 4 hrs |
| Melt Temperature (PA66) | 280 - 300 °C |
| Mold Temperature (PA6) | 250 - 290 °C |
| Mold Temperature | 80 - 120 °C |
| Shrinkage Rate | 1.0 - 2.0% |
PDF Download
Antistatic PA6 Technical Datasheet
Download the complete technical datasheet including mechanical, thermal, and processing properties.
Download PDF