PA6 GF15
Polyamide PA6 GF15
PA6 GF15 is a glass fiber reinforced nylon 6 material containing 15% glass fiber reinforcement. Compared with standard PA6, it provides higher mechanical strength, improved rigidity, better dimensional stability, and enhanced heat resistance. It is widely used for structural components, automotive parts, industrial gears, electrical components, and precision injection molded applications.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 120 MPa |
| Tensile Modulus | 6500 MPa |
| Elongation at Break | 3 - 5% |
| Flexural Strength | 180 MPa |
| Flexural Modulus | 5500 MPa |
| Hardness (Rockwell) | R120 / R125 |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point | 215 - 225 °C |
| HDT (1.82 MPa) | 170 - 190 °C |
| Continuous Use Temp | 100 - 120 °C |
| Flammability (UL94) | HB (V-0 grades available) |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 °C |
| Drying Time | 4 - 6 hrs |
| Melt Temperature | 250 - 280 °C |
| Mold Temperature | 80 - 120 °C |
| Injection Pressure | 80 - 140 MPa |
| Shrinkage Rate | 0.3 - 0.6% |