PA6 Flame Retardant GF30
Flame Retardant Glass Fiber Reinforced Polyamide PA6 GF30
PA6 Flame Retardant GF30 is a 30% glass fiber reinforced nylon 6 material with enhanced flame resistance, high strength, excellent rigidity, and dimensional stability. It is widely used in electrical components, automotive parts, industrial structures, and applications requiring safety and reliable performance.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 170 - 190 MPa |
| Tensile Modulus | 8500 - 9500 MPa |
| Elongation at Break | 3 - 5% |
| Flexural Strength | 260 - 300 MPa |
| Flexural Modulus | 8000 - 9000 MPa |
| Impact Strength (Izod, Notched) | 8 - 12 kJ/m² |
| Hardness (Rockwell) | R120 / R125 |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point | 215 - 225 °C |
| HDT (1.82 MPa) | 180 - 220 °C |
| Continuous Use Temp | 120 - 140 °C |
| Flammability (UL94) | V-0 |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 - 90°C |
| Drying Time | 4 - 6 hrs |
| Melt Temperature | 250 - 280 °C |
| Mold Temperature | 80 - 120 °C |
| Injection Pressure | 100 - 160 MPa |
| Shrinkage Rate | 0.2 - 0.5% |