Halogen-Free Red Phosphorus Flame Retardant PA6
Halogen-Free Red Phosphorus Flame Retardant Polyamide PA6
Halogen-Free Red Phosphorus Flame Retardant PA6 is a modified nylon 6 material developed for applications requiring excellent flame resistance and safety performance. It provides high mechanical strength, good electrical insulation, and reliable thermal stability for electronic, automotive, and industrial components.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 70 - 90 MPa |
| Tensile Modulus | 2500 - 3500 MPa |
| Elongation at Break | 3 - 8% |
| Flexural Strength | 110 - 140 MPa |
| Flexural Modulus | 3000 - 4000 MPa |
| Impact Strength (Izod, Notched) | 4 - 8 kJ/m² |
| Hardness (Rockwell) | R110 / R120 |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point | 215 - 225 °C |
| HDT (1.82 MPa) | 80 - 120 °C |
| Continuous Use Temp | 100 - 120 °C |
| Flammability (UL94) | V-0 |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 - 90°C |
| Drying Time | 4 - 6 hrs |
| Melt Temperature | 240 - 270 °C |
| Mold Temperature | 70 - 100 °C |
| Injection Pressure | 80 - 140 MPa |
| Shrinkage Rate | 0.8 - 1.5% |