Toughened Low Temperature Resistant PA66
Toughened Modified Polyamide PA66
Toughened Low Temperature Resistant PA66 is a modified nylon 66 material designed to maintain excellent impact strength and toughness under low-temperature conditions. It provides improved resistance to cracking, good mechanical performance, and reliable durability for automotive, industrial, and outdoor applications.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 65 - 80 MPa |
| Tensile Modulus | 1800 - 2600 MPa |
| Elongation at Break | 50 - 150% |
| Flexural Strength | 80 - 110 MPa |
| Flexural Modulus | 2000 - 2800 MPa |
| Impact Strength (Notched) | 15 - 35 kJ/m² |
| Impact Strength at -30°C | 10 - 25 kJ/m² |
| Hardness (Rockwell) | R90 / R115 |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point | 255 - 265 °C |
| HDT (1.82 MPa) | 70 - 100 °C |
| Continuous Use Temp | 100 - 120 °C |
| Flammability (UL94) | HB (V-0 grades available) |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 - 90°C |
| Drying Time | 4 - 6 hrs |
| Melt Temperature | 270 - 300 °C |
| Mold Temperature | 80 - 120 °C |
| Injection Pressure | 80 - 140 MPa |