PA6 GF Flame Retardant Toughened Low Temperature Resistant
Glass Fiber Reinforced Flame Retardant Toughened Polyamide PA6
PA6 GF Flame Retardant Toughened is a modified nylon 6 material combining glass fiber reinforcement, flame resistance, and improved low-temperature toughness. It provides high strength, excellent impact resistance, dimensional stability, and reliable performance in demanding automotive, electrical, and industrial applications.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 150 - 180 MPa |
| Tensile Modulus | 7500 - 9500 MPa |
| Elongation at Break | 4 - 8% |
| Flexural Strength | 240 - 280 MPa |
| Flexural Modulus | 7500 - 9000 MPa |
| Impact Strength (Notched) | 12 - 20 kJ/m² |
| Impact Strength at -30°C | 8 - 15 kJ/m² |
| Hardness (Rockwell) | R115 / R125 |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point | 215 - 225 °C |
| HDT (1.82 MPa) | 180 - 220 °C |
| Continuous Use Temp | 120 - 140 °C |
| Flammability (UL94) | V-0 |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 - 90°C |
| Drying Time | 4 - 6 hrs |
| Melt Temperature | 250 - 280 °C |
| Mold Temperature | 80 - 120 °C |
| Injection Pressure | 100 - 160 MPa |
PDF Download
PA6 GF Flame Retardant Toughened Low Temperature Resistant Technical Datasheet
Download the complete technical datasheet including mechanical, thermal, and processing properties.
Download PDF