PA66 GF20
Glass Fiber Reinforced Polyamide PA66 GF20
PA66 GF20 is a 20% glass fiber reinforced nylon 66 material offering improved strength, rigidity, dimensional stability, and heat resistance compared with standard PA66. It is widely used for automotive components, electrical parts, industrial structures, and precision injection molded applications.
Techinherit — With over 20 years of experience in the plastics industry, we have a professional R&D laboratory. We have developed thousands of customized material formulations and solved tens of thousands of application challenges. Holding multiple modified plastic patents, we are a manufacturing enterprise dedicated to plastic R&D, production, and sales.
Applications
Properties
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength | 150 - 170 MPa |
| Tensile Modulus | 6500 - 7500 MPa |
| Elongation at Break | 3 - 6% |
| Flexural Strength | 220 - 250 MPa |
| Flexural Modulus | 6000 - 7000 MPa |
| Impact Strength (Notched) | 8 - 12 kJ/m² |
| Hardness (Rockwell) | R115 / R125 |
Thermal Properties
| Property | Value |
|---|---|
| Melting Point | 255 - 265 °C |
| HDT (1.82 MPa) | 220 - 240 °C |
| Continuous Use Temp | 120 - 140 °C |
| Flammability (UL94) | HB (V-0 grades available) |
Processing Parameters
| Property | Value |
|---|---|
| Drying Temperature | 80 - 90°C |
| Drying Time | 4 - 6 hrs |
| Melt Temperature | 280 - 300 °C |
| Mold Temperature | 80 - 120 °C |
| Injection Pressure | 100 - 160 MPa |